Title: FabricationandmagneticresponseprobedbyRFtransversesusceptibility in La0.67Ca0.33MnO3 nanowires
Authors: Chandra, S
Figueroa, A I
Ghosh, Barnali
Raychaudhuri, A K
Phan, M H
Mukherjee, P
Srikanth, H
Keywords: Manganites
Nanowires
Magnetic anisotropy
Issue Date: 2012
Publisher: Physica B
Citation: S. Chandra , A. I. Figueroa, B. Ghosh , A. K. Raychaudhuri , M. H. Phan, P. Mukherjee , H. Srikanth, Fabrication and magnetic response probed by RF transverse susceptibility in La0.67 Ca0.33MnO3 nanowires, Physica B, 2012, 407, 175
Abstract: The temperature and magnetic field dependence of the radio-frequency(RF) transverse susceptibility(χT) of La0.67Ca0.33MnO3 crystalline nanowires has been studied using a very sensitive self-resonant tunnel-diode oscillator (TDO) technique.The nanowires were synthesized using porous templates of anodized alumina by chemical solution deposition technique,and the crystalline nature of the nanowires with the average diameter of 70nm was confirmed by TEM, SAED, and HREM. RF transverse susceptibility experiments reveal the presence of a double-peak structure at T≤245K (the Curie temperature) but a single peak at T>245K. This distinguishes the low temperature ferromagnetic state from the high temperature paramagnetic state. The effective magnetic anisotropy field(HK), which corresponds to the peak location of χT, has been found to increase with decrease in temperature from the Curie temperature.
URI: http://hdl.handle.net/123456789/39
Appears in Collections:2012

Files in This Item:

File Description SizeFormat
Fabrication and magnetic.pdf634.98 kBAdobe PDFView/Open

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

 

Valid XHTML 1.0! DSpace Software Copyright © 2002-2010  Duraspace - Feedback